Original Article

Linear Expansion and Durability of a Composite Boards (MDF Laminated Using Three Selected Wood Veneers) against Drywood Termites

Tekat Dwi CAHYONO2,, Hikma YANTI3, Laela Nur ANISAH4, Muh Yusram MASSIJAYA5, Apri Heri ISWANTO6
Author Information & Copyright
2Faculty of Agriculture and Forestry, University of Darussalam Ambon, Jl. Raya Waehakila Puncak Wara, Sirimau, Ambon 97128, Indonesia
3Faculty of Forestry, Tanjungpura University, Jl. Prof. Hadari Nawawi, Pontianak 78121, Indonesia
4Indonesian Ministry of Environment and Forestry, Manggala Wanabakti Building, Jl. Jend. Gatot Subroto, Jakarta 10270, Indonesia
5Department of Forest Product, Faculty of Forestry, IPB University, Jl. Raya Dramaga, Bogor 16680, Indonesia
6Department of Forest Product, Faculty of Forestry, Universitas Sumatera Utara, Padang Bulan, Medan 20155, Indonesia
Corresponding author: Tekat Dwi CAHYONO (e-mail: tekatdwicahyono@gmail.com, ORCID: 0000-0002-3010-7656)

© The Korean Society of Wood Science & Technology.

Received: Apr 16, 2020; Accepted: Nov 06, 2020

Published Online: Nov 25, 2020

Abstract

This research was conducted to investigate the linear expansion and resistance properties of a composite board (com-ply). This board was made of medium-density fiberboard (MDF) laminated using avocado (Persea americana), mahogany (Swietenia mahogani), and pine (Pinus merkusii) veneers. These three types of veneers were laminated on both surfaces of the MDF using adhesives, namely, epoxy and isocyanate. Glue (250 g·m−2) was spread on the surface, followed by cold press for 3 h with an applied pressure of 15 kg·cm−2. The research result revealed that com-ply exhibited an increased dimensional stability compared with MDF, indicated by reduction in water absorption, thickness swelling, and linear expansion. The com-ply made of the pine veneer and isocyanate adhesive exhibited high density, water absorption, thickness swelling, and screw withdrawal load. The com-ply that exhibited the strongest resistance to drywood termite attacks was the one made of the mahogany veneer and isocyanate adhesive. Moreover, the com-ply that exhibited the biggest weight loss (3.6 %) was made of the pine veneer and epoxy adhesive. The results of this research may facilitate in manufacturing com-ply using the selected veneer and adhesive without the application of hot press.

Keywords: com-ply; resistance; linear expansion; MDF; veneer

1. INTRODUCTION

Hundreds of millions meter cubic of wood-based panels are produced each year throughout the world. One of them is fiberboard. The fiberboard production growth increased by 44 % within 2011-2014 period and 82 % of the world’s fiberboard production was medium density fiberboard (MDF). Since 2011, its production had grown on average 6 % per year (FAO, 2016). China is the world’s leading MDF producers and users. Indonesia’s fiberboard production in 2017 was 449,492.81 m3 (BPS, 2017). The strength of this product lied in its use of varied raw materials and industrial wastes (Hiziroglu et al., 2007; Garcia et al., 2018). In its production process, some MDF types were laminated with melamine, polyvinyl chloride, veneer and other materials to improve the surface appearance and other physical, mechanical qualities (Kılıç et al., 2009; Jocham et al., 2011; Taghiyari and Norton, 2014).

The veneer laminated to MDF surface is widely open in the future. This is because the world’s woodbased panel production is still dominated by veneer and plywood. In 2015, its production had reached 171 million m3 (39 % of the total wood-based panel production), increasing 49 % from 2011 (FAO, 2016). The veneer and plywood productions in Indonesia in 2017 were 4.8 % and 11.1 % respectively of the total woodbased panel (BPS, 2017). While raw material procurement might be an issue, it can be solved using the right approach, such as utilizing fast-growing woods (Rowell, 1998; Cahyono and Masssijaya, 2007; Cahyono et al., 2015). Moreover, previous studies on increased flexural properties after the process of laminated composite board with veneer had provided some support (Biblis et al., 1996; Büyüksarý et al., 2012; Cahyono et al., 2019).

This research manipulated MDF into composite board (com-ply) by adding avocado, pine and mahogany veneer on the face and back parts. Avocado veneer was available with affordable price but less frequently used as the laminating materials. Meanwhile, pine and mahogany veneer had more attractive and good appearance. Those three veneer types had good dimensional stabilization and were proven capable of improving the physical, mechanical, and durability properties when utilized to laminate the oriented strand board (Yanti et al., 2019). Com-ply improved the benefits of panel products into structural materials and expanded its utilization. This research aimed at evaluating comply physical properties, linear expansion, internal bonding, screw withdrawal load and resistance against drywood termite’s attack. The research results provided alternative attempts to improve MDF’s surface appearance, physical properties, strength and durability against biological destruction agent attack.

2. MATERIALS and METHODS

2.1. Materials

Medium density fiberboard (MDF) used in this research was produced by the Indonesia Fiberboard Industry Ltd. The board obtained from the local market had the size of 244 cm × 122 cm × 1 cm (length, width, thickness). The adhesive for MDF consisted of phenol formaldehyde and solid content adhesive of 42.5±2%. The MDF laminating materials were avocado (Persea americana), mahogany (Swietenia mahogany), and pine (Pinus merkusii) veneers. Those three veneers were obtained from the local market and the veneer thickness was 1.52±0.08 mm. The moisture content of veneer and MDF before adhered was respectively by 7.4±0.62% and 12.2±1.2%. The density of pine, mahogany and avocado veneer was respectively 587±23.22 kg·m-3, 516±35.19 kg·m-3, and 543±14.21 kg·m-3.

The adhesives used were isocyanate and epoxy. Both adhesives consisted of base and hardener with the composition of 100:12 for isocyanate and 100:100 for epoxy. The base type and hardener of isocyanate adhesive were respectively PI-127T and H3M. Both adhesive types were produced by Poly Oshika Ltd. and the Solid Content was respectively 43±3% and 98±0.5%. The viscosity of PI-127T (ps/25 °C) was 150 ps and 1.5 ps for H3M. Epoxy Adhesive used the base type of AD-102 and hardener type of VR-502. Those adhesives were made by Fox Ltd.

2.2. Development of composite board

Table 1 showed the composition of the veneer and adhesives. Each type of veneers was used to laminate both MDF (face and back) surfaces with a combination of two types of adhesive. The test sample size was 35 cm × 35 cm and the adhesive glue spread was 250 g·cm-2. Cold press was applied for 3 hours at 15 kg·cm-2 press pressure. Afterwards, a conditioning was applied for two weeks and followed with test sample cutting based on each testing standard. Conditioning was conducted at the room temperature (25 °C) and relative humidity (RH) 85 %.

Table 1. Com-ply Types
Num. Type Adhesive Face and Back Veneer
1 MDF - -
2 AMI Isocyanate Avocado
3 AME Epoxy Avocado
4 PMI Isocyanate Pine
5 PME Epoxy Pine
6 MMI Isocyanate Mahogany
7 MME Epoxy Mahogany
Download Excel Table
2.3. Testing of physical and mechanical properties

The testing of physical properties was conducted on density, moisture content, water absorbtion, thickness swelling and linear expansion (parallel and perpendicular). Density was measured based on the oven-dry weight, while the test sample’s length and width were 10 cm × 10 cm. The test sample’s moisture content and water absorption were 10 cm × 10 cm (length, width), while the test sample’s thickness swelling and linear expansion were 5 cm × 5 cm (length, width). Next, the mechanical properties tested was screw withdrawal load (SWL) and internal bonding (IB). The used standard was JIS A 5905-2003 (JSA, 2003). The SWL test sample’s length and width were 5 cm × 10 cm, while the IB test sample’s length and width were 5 cm × 5 cm.

2.4. The durability of com-ply to the drywood termites' attacks

The testing of resistance to drywood termites (Cryptotermes cynocephalus) was performed based on SNI 01-7207-2006 standard (BSN, 2006). Fifty worker termites were placed in a glass tube in all com-ply surfaces. The test sample size used was 2.5 cm × 5.0 cm (length and width), and the thickness followed the com-ply thickness. The com-ply resistance to termites attack was analyzed based on the weight loss percentage and the drywood termite mortality for 12 weeks feeding.

2.5. Data analysis

This research used completely randomized design with 7 treatments (com-ply types) and five repetitions. The general model of this design wasas presented by Gaspersz (1991). If the difference in com-ply types was significant, it was then followed with Duncan advanced test to see the best type.

3. RESULTS and DISCUSSION

3.1. Moisture content and density

The mean moisture content (MC) of all com-ply types, including MDF, was 12.32 % at 1.33 % standard deviation. The moisture content of each com-ply type was presented in Table 2. The analysis of variance result showed that com-ply type had an influence on MC (p = 0.000). Table 3 shows com-ply had relatively high mean moisture content, including PMI (pine, isocyanate adhesives), AMI (avocado, isocyanate adhesives), and MME (mahony, epoxy adhesives). The laminating veneer thinner than MDF was easier to reach the Equilibrium Moisture Content. Furthermore, the com-ply types of MMI (mahony, isocyanate adhesives), PME (pine, epoxy adhesives) and AME (avocado, epoxy adhesives) seen having smaller MC when compared to MDF. The addition of adhesive between veneer and MDF resulted in the com-ply’s hygroscopic changes. The isocyanate adhesive was bonded with the wood hydroxyl group that its reactivity decreased (Nuryawan and Alamsyah, 2017). Beside those factors, the moisture content of composite board was influenced by density and the MC raw materials.

Table 2. Moisture content and density of com-ply
Type of Com-ply MCs (%) Ds (kg•m-3)
MDF 12.22 ± 0.39 653 ± 14.63
MMI 13.36 ± 0.22 619 ± 7.83
MME 10.57 ± 0.45 650 ± 20.87
AMI 13.60 ± 0.90 621 ± 5.55
AME 11.93 ± 0.46 632 ± 5.57
PMI 13.63 ± 0.32 695 ± 16.80
PME 11.04 ± 0.40 678 ± 16.25

s = significance (p ≤ 0.05)

Download Excel Table
Table 3. Duncan analysis for moisture content
Type of Com-ply N Subset
1 2 3 4
MMI 5 10.5680
PME 5 11.0420 11.0420
AME 5 11.9340 11.9340
MDF 5 12.2180
PMI 5 13.2740
AMI 5 13.6040
MME 5 13.6040
Sig. 0.307 0.060 0.538 0.501

Means for groups in homogeneous subsets are displayed.

Based on observed means.

The error term is Mean Square (Error) = 0.518.

Download Excel Table

The com-ply density increased the laminated pine veneer ranging between 2.7 % and 7.7 %. The analysis of variance result indicated that veneer layer addition influenced density (p = 0.000). Duncan advanced test placed com-ply PMI as the greatest increase mean than the other types (Table 4). The laminated veneer to composite board surface was more likely to increase the density although there was a same value with MDF and even there was a lower one. It was because of the different materials used as the layer (Yanti et al., 2019). Pine has the highest density as compared to avocado and mahogany (Karlinasari et al., 2010). The second causes were gluing and pressing during production process (Zhang et al., 2018; Cahyono et al., 2020). The adhesive addition might add the com-ply’s weight, while the compression had the potential to change the density when changing the material properties, such as the occurrence of densification. These phenomena formed due to the mechanical power and interaction between adhesive and wood cells. Cristescu (2006) explained that during the compression process, most fibers located in the area of gluelines lost their luminary, approximated each other, and resulted in higher density.

Table 4. Duncan analysis for density
Type of Com-ply N Subset
1 2 3 4
MMI 5 6.1880E2
PME 5 6.2060E2
AME 5 6.3240E2 6.3240E2
MDF 5 6.5040E2 6.5040E2
PMI 5 6.5340E2
AMI 5 6.7840E2
MME 5 6.9540E2
Sig. 0.195 0.073 0.759 0.090

Means for groups in homogeneous subsets are displayed.

Based on observed means.

The error term is Mean Square (Error) = 233.929.

Download Excel Table
3.2. Water Absorption (WA), Thickness Swelling (TS) and Linear Expansion (LE)

Water absorptions of MDF and com-ply are shown in Fig. 1. It was seen that MDF had greater WA than the other 6 types. The analysis of variance result showed that com-ply type influenced WA during 24-hour immersion, with no influence occuring during 2-hour immersion. The Duncan test suggested that PME had the lowest WA than all com-ply types. Tsoumis (1991) has presented the fact that when wood is immersed in water, the active water movement may occur through the cell cavities. If the immersion is continuously made, the cell cavities will be saturated in water. Thus, the immersion period and density of the laminating materials contributed in WA difference.

wood-48-6-907_F1
Fig. 1. Water Absorption of Com-ply.
Download Original Figure

The high mean thickness swelling (TS) value was dominated by MDF and PMI type com-ply (pine veneer, isocyanate adhesive). This type even had greater TS value than MDF in 2-hour immersion, even though after 24-hour immersion, the opposite occured (Fig. 2). In 2-hour immersion, the lowest TS was found in MME type and after 24-hour immersion was found in PME. MDF laminating using pine veneer and epoxy adhesive (PME type) was able to reduce the value of TS up to 68 %. Some contradictive phenomena happened in PMI, while the TS decrease was only 4 % at the end of 24-hour immersion. The phenomena started to be seen from the WA value which was bigger than the MDF value, especially when the 2-hour immersion was performed. During the 24-hour immersion, the WA value was more than 40 %.

wood-48-6-907_F2
Fig. 2. Thickness swelling of com-ply.
Download Original Figure

After being immersed for two hours, it is found that the parallel linear expansion (PLE) value of AMI type com-ply is the higher than MDF and other com-ply (Table 5). Yet, after the immersion proceeds for 24 hours, MDF had the highest PLE. It was also seen the decreased PLE of MMI, MME, AMI and AME type com-ply after 2- and 24-hour immersions. Similar trend also occurred in perpendicular linear expansion (PpLE). Three com-ply types (MMI, AMI, PMI) had their PpLE increased and the other three had decreased after 2-hour immersion. After 24-hour immersion, MDF had the highest PpLE value. These increase and decrease in PLE and PpLE values were statistically insignificant, both during 2- and 24-hour immersions (Table 5).

Table 5. Water Absorption, Thickness Swelling and Linear Expansion of Com-ply
Type of Com-ply Water Absorption (%) Thickness Swelling (%) Linear Expansion
Parallel Perpendicular
2ns Hour 24sHour 2s Hour 24sHour 2ns Hour 24ns Hour 2ns Hour 24ns Hour
MDF 22.3 ± 14.3 52.0 ± 9.5 3.90 ± 2.35 12.82 ± 1.17 0.21 ± 0.05 0.52 ± 0.07 0.37 ± 0.10 0.86 ± 0.25
MMI 17.8 ±7.1 41.8 ± 12.0 2.00 ± 1.17 7.57 ± 2.59 0.17 ± 0.06 0.38 ± 0.08 0.43 ± 0.03 0.68 ± 0.19
MME 12.0 ± 4.3 32.9 ± 7.4 1.20 ± 0.62 6.58 ± 2.97 0.18 ± 0.13 0.39 ± 0.05 0.33 ± 0.11 0.66 ± 0.17
AMI 18.0 ± 8.5 45.2 ± 8.2 1.26 ± 1.03 6.15 ± 2.39 0.26 ± 0.07 0.44 ± 0.10 0.45 ± 0.18 0.72 ± 0.24
AME 17.0 ± 8.9 41.1 ± 11.0 2.02 ± 1.20 6.33 ± 3.11 0.18 ± 0.12 0.39 ± 0.10 0.39 ± 0.19 0.73 ± 0.27
PMI 28.7 ± 17.0 44.8 ± 12.1 5.90 ± 4.10 12.26 ± 3.08 0.14 ± 0.05 0.30 ± 0.08 0.41 ± 0.24 0.81 ± 0.12
PME 10.0 ± 0.7 26.0 ± 5.0 1.24 ± 0.55 4.75 ± 0.63 0.22 ± 0.07 0.41 ± 0.09 0.38 ± 0.09 0.57 ± 0.10

s significant (p ≤ 0.05)

ns insignificant (p > 0.05)

Download Excel Table

The two main factors of LE were materials and manufacture process. The different wood types and particle orientations were the main causes of LE difference. It was the case particularly in composite panel comprising of particles (Wu and Suchsland, 1996; Iswanto et al., 2017). If the materials were relatively homogenous, for example fiberboard, then the LE difference was tightly related to the product density (Ganev et al., 2007; Ayrilmis, 2008). The manufacture process factors included adhesive type, thickness, and heat treatment (Xu and Suchsland, 1997; Miyamoto et al., 2002; Zhang et al., 2018).

Fig. 3 showed the linear regression between water absorption and thickness swelling. The relationship of these parameters was linear with a high determination value (R2 = 0.7964). The regression between water absorption and linear expansion (LE) was presented in Fig. 4. Both parameters seemed to influence each other since their R2 values for, parallel and perpendicular ones, were 0.66 and 0.71 respectively. Furthermore, it might be seen that perpendicular LE had a greater value than the parallel one. The difference between the two was consistent in all com-ply types, during 2- and 24-hour immersions. The value difference for 2-hour immersion was 128.7±108.9% and for 24-hour immersion was less than that, i.e. 78.8±48.1%. This percentage value confirmed the previous study’s result which found that PpLE was greater than PLE (Wu and Suchsland, 1996).

wood-48-6-907_F3
Fig. 3. Thickness Swelling of Com-ply based on Water Absorption Changes.
Download Original Figure
wood-48-6-907_F4
Fig. 4. Linear Expansion of Com-ply based on Water Absorption Changes.
Download Original Figure

Linear Expansion and TS occurred due to the changes of fiber walls in different MC conditions (Ganev et al., 2007). When explaining the influence of density on LE, in fact it was not congruent. Some presented that there was no relationship, such as in particleboard (Hiziroglu and Suchsland, 1993; Milagres et al., 2019), and MDF (Xu and Suchsland, 1997). However, some have presented the data in contradiction (Ayrilmis et al., 2017, Seo et al., 2019, Taskirawati et al., 2019). Thus, beside increasing the dimensional stability, the laminated MDF with avocado, mahogany, and pine veneer asserted a close relationship between WA and TS, especially the com-ply products. Second, the close relationship between WA and LE. Third, density changes influenced LE com-ply.

3.3. Screw Withdrawal Load (SWL) and Internal Bonding (IB)

Fig. 5 indicated the screw withdrawal load (SWL) difference between MDF and com-ply. MDF laminated using veneer was expected to contribute to SWL increase. In fact, one com-ply type (AMI type) was excluded from the standards while other com-ply values were above the standard which requires SWL value > 500 N. The analysis of variance showed that com-ply type had an influence on SWL value (p = 0.000). Duncan test determined that PMI type com-ply had the highest SWL value, and the lowest one was AMI type (Avocado veneer, Isocyanate adhesive). Compared to MDF, the SWL increase of PMI type com-ply was 37.8 %. Other types had nearly similar means (Table 6). This result asserted that although one type was not included in standard, MDF laminating using avocado, mahogany and pine veneer was recommended to improve SWL.

Table 6. Duncan analysis for Screw Withdrawal Load
Type of Com-ply N Subset
1 2 3
MMI 5 30.9360
PME 5 42.5260
AME 5 42.6740
MDF 5 42.9805
PMI 5 43.3380
AMI 5 49.5320
MME 5 59.2280
Sig. 1.000 0.060 1.000

Means for groups in homogeneous subsets are displayed.

Based on observed means.

The error term is Mean Square (Error) = 26.017.

Download Excel Table
wood-48-6-907_F5
Fig. 5. Screw Withdrawal Load of Com-ply.
Download Original Figure

MDF’s internal bonding was 0.35 ± 0.09 N·mm-2 and the IB of all com-ply types was 0.29 ± 0.11 N·mm-2. The complete values might be seen in Fig. 6. All com-ply types had lower IB values than MDF, yet the differences were statistically insignificant (p = 0.647). This was because during the testing, the part undergoing damage was the middle layer of composite board (MDF), thus it might be said that all those values were the IB value of MDF. The veneer parts glued using isocyanate and epoxy adhesive were not damaged. The requirement of minimum IB to meet JIS standard was 0.5 N·mm-2. Based on this requirement, all com-ply types in this research failed to meet the standards. Furthermore, low IB also gave the contribution to TS. Fig. 6 shows that PMI had the lowest IB. One of its implications was seen from the high WA and TS value.

wood-48-6-907_F6
Fig. 6. Internal Bonding of Com-ply.
Download Original Figure
3.4. Resistance against drywood termites

The wood and wood panel's resistance to drywood termites was classified into 5 categories (BSN, 2006). If the weight loss (WL) was less than 2 %, then it was classified as highly resistant. Weight losses between 2.0 and 4.4 % were classified as resistant. Table 7 showed that MDF, MME, AMI and PME type com-ply were classified as resistant to attack, while other types were classified as highly resistant.

Table 7. Weight Loss and Mortality of all comp-ly types
Type of Com-ply Weight Lossns (%) Mortalitys (%)
MDF 2.6 ± 0.6 98.0 ± 3.1
MMI 1.6 ± 0.6 94.8 ± 8.5
MME 2.1 ± 0.5 96.4 ± 2.3
AMI 2.4 ± 0.2 86.8 ± 7.0
AME 1.7 ± 0.3 92.8 ± 4.1
PMI 2.0 ± 0.3 87.2 ± 8.8
PME 3.6 ± 2.5 76.0 ± 10.4

s significant (p ≤ 0.05)

ns insignificant (p > 0.05)

Download Excel Table

During the test of resistance, drywood termites were placed on the test sample surface. As an implication, the laminated material constitutes the main factor which influenced its resistance to termites attack. The veneer of the three wood types used to laminate MDF might endure the attack level well. It was proven that the com-ply type of MMI (mahogany, isocyanate adhesives) had smaller weight loss. The MDF was laminated using avocado veneer and epoxy adhesive (AME type) increase the durability of MDF from resistant to highly resistant category. Com-ply types of AMI, PMI, and MME also had WL which was smaller than MDF. The only com-ply having WL higher than MDF was PME. However, the decreasing value of WL was statistically insignificant. The WL differences in the same wood types were caused by the veneer conditions. The pine wood part closing to the pith had the WL of more than 2 %, while the part closing to the bark, the value was less than 2 %. The durability of Mahogany wood from the drywood termites' attacks was categorized into highly resistant (WL < 2 %) both in heartwood and sapwood part (Septiana et al., 2014).

After attacking the surface, the termite would slowly attack the inside part. Isocyanate and epoxy adhesives served the purpose of making a hindrance in case the attack began to take place to the com-ply's middle part. The termite attack activities were inhibited as shown from the mortality which was more than 70 %. It was asserted with the termite mortality which was statistically significant (p = 0.002).

4. CONCLUSION

Laminated MDF using avocado, pine and mahogany veneers decreased the hygroscopic properties and increased its resistance to the drywood termites' attacks. The increasing com-ply's density was influenced by the used veneer type. Most linear expansion decreased, yet two com-ply types were found increased. These happened both in parallel and perpendicular direction, yet statistically insignificant. The decreasing TS after laminated with veneers showed that the com-ply's dimensional stability increased. SWL also increased up to 37.8 % in the PMI com-ply type, while the internal bonding was the same with MDF.

References

1.

Ayrilmis N. Effect of compression wood on dimensional stability of medium density fiberboard. Silva Fennica. 2008; 42(2):285.

2.

Ayrilmis N., Akbulut T., Yurttaş E. Effects of core layer fiber size and face-to-core layer ratio on the properties of three-layered fiberboard. BioResources. 2017; 12(4):7964-7974.

3.

Biblis E.J., Grigoriou A., Carino H. Flexural properties of veneer-overlaid OSB composite panels from southern yellow pine. Forest Products Journal. 1996; 46(4):59-62.

4.

BPS Statistik Produksi Kehutanan (Statistic of Forestry Production) 2017. Sub-Directorate of Forestry Statistic (Ed). BPS-Statistics Indonesia, Jakarta, Indonesia. 2017

5.

BSN 01-7207-2006: Uji ketahanan kayu dan produk kayu terhadap organisme perusak kayu (The durability test of wood and wood products against wood-deterioration organisms). BSN (Badan Standarisasi Nasional) (National Standardization Agency of Indonesia). 2006; p. 12

6.

Büyüksarı Ü., Hiziroglu S., Akkılıç H., Ayrılmış N. Mechanical and physical properties of medium density fiberboard panels laminated with thermally compressed veneer. Compos Part B-Eng. 2012; 43(2):110-114.

7.

Cahyono T.D., Darmawan W., Novriyanti E. Performance of samama (Anthocephalus macrophyllus) LVL based on veneer thickness, juvenile proportion and lay-up. Wood Material Science & Engineering. 2020; 15(3):155-162.

8.

Cahyono T.D., Massijaya M.Y., Iswanto A.H., Yanti H., Anisah L.N. The flexural properties of medium density fibreboard overlaid with veneer from three species of wood. IOP Conf. Ser.: Earth and Environmental Science. 2019; 374:012061.

9.

Cahyono T.D., Masssijaya M.Y. Laminated Veneer Lumber (LVL): Sejarah, Penggunaan dan Teknologi (LVL: History, Utilization and Technology). 2007 Bogor, Indonesia: Fakultas Kehutanan IPB (Faculty of Forestry, Bogor Agricultural University) Press. .

10.

Cahyono T.D., Wahyudi I., Priadi T., Febrianto F., Darmawan W., Bahtiar E.T., Ohorella S., Novriyanti E. The quality of 8 and 10 years old samama wood (Anthocephalus macrophyllus). Journal of the Indian Academy of Wood Science. 2015; 12(1):22-28.

11.

Cristescu C. Bonding of laminated veneers with heat and pressure only. 2006 In: International Conference on Environmentally-Compatible Forest Products: 20/09/2006-22/09/2006, Fernando Pessoa University.

12.

FAO 2015 Global Forest Products Facts and Figures. 2016Food And Agriculture Organization of The UN. .

13.

Ganev S., Cloutier A., Beauregard R., Gendron G. Linear expansion and thickness swell of MDF as a function of panel density and sorption state. Wood and Fiber Science. 2007; 37(2):327-336.

14.

Garcia C.M., San Pablo M.R., Bianchi S., Pichelin F. Resistance of fibreboards made of milled coconut husk and bonded with tannin against insects and fungi under Philippine conditions. International Wood Products Journal. 2018; 9(3):99-107.

15.

Gaspersz V. Metode Perancangan Percobaan Untuk Ilmu-Ilmu Pertanian, Ilmu-Ilmu Teknik, dan Biologi. 1991 Bandung, Indonesia: CV. Armico. .

16.

Hiziroglu S., Bauchongkol P., Fueangvivat V., Soontonbura W., Jarusombuti S. Selected properties of medium density fiberboard (MDF) panels made from bamboo and rice straw. Forest Products Journal. 2007; 57(6):46-50.

17.

Hiziroglu S., Suchsland O. Linear expansion and surface stability of particleboard. Forest Products Journal. 1993; 43(4):31.

18.

Iswanto A.H., Aritonang W., Azhar I., Fatriasari W. The physical, mechanical and durability properties of sorghum bagasse particleboard by layering surface treatment. Journal of the Indian Academy of Wood Science. 2017; 14(1):1-8.

19.

Jocham C., Schmidt T.W., Wuzella G., Teischinger A., Kandelbauer A. Adhesion improvement of powder coating on medium density fibreboard (MDF) by thermal pre-treatment. Journal of Adhesion Science and Technology. 2011; 25(15):1937-1946.

20.

JSA A 5905-2003: Fibreboard. Japanese Industrial Standards. 2003 Tokyo, Japan: Japanese Standard Association (JSA). .

21.

Karlinasari L., Nawawi D., Widyani M. Kajian Sifat Anatomi dan Kimia Kayu Kaitannya dengan Sifat Akustik Kayu. Bionatura. 2010; 12(3):110-116.

22.

Kılıç M., Burdurlu E., Aslan S., Altun S., Tümerdem Ö. The effect of surface roughness on tensile strength of the medium density fiberboard (MDF) overlaid with polyvinyl chloride (PVC). Materials & Design. 2009; 30(10):4580-4583.

23.

Komariah R.N., Massijaya M.Y. Physical- Mechanical Properties of Glued Laminated Timber Made from Tropical Small-Diameter Logs Grown in Indonesia. Journal of the Korean Wood Science and Technology. 2015; 43(2):156-167.

24.

Milagres E.G., Barbosa R.A.G.S., Caiafa K.F., Gomes G.S.L., Castro T.A.C., Vital B.R. Properties of Particleboard Panels Made of Sugarcane Particles With and Without Heat Treatment. Revista Árvore. 2019; 43(5).

25.

Miyamoto K., Suzuki S., Inagaki T., Iwata R. Effects of press closing time on mat consolidation behavior during hot pressing and on linear expansion of particleboard. Journal of Wood Science. 2002; 48(4):309-314.

26.

Nuryawan A., Alamsyah E.M. A review of isocyanate wood adhesive: a case study in Indonesia. Applied Adhesive Bonding in Science and Technology. 2017; :73-90.

27.

Rowell R.M. The state of art and future development of bio-based composite science and technology towards the 21st century. 1998

28.

Seo Y-R., Kim B-J., Lee S-Y. Effects of Nanoclay and Glass Fiber on the Microstructural, Mechanical, Thermal, and Water Absorption Properties of Recycled WPCs. Journal of the Korean Wood Science and Technology. 2019; 47(4):472-485.

29.

Septiana D., Febrianto F., Arinana. Keawetan Alami Dua Belas Jenis Kayu dari Hutan Pendidikan Gunung Walat terhadap Serangan Rayap (Natural Durability of 12 Woods Species Grown in Mount Walat Forest Education against Termites Attacked). Thesis. 2014 Bogor(ID): IPB University. .

30.

Taghiyari H.R., Norton J. Effect of silver nanoparticles on hardness in medium-density fiberboard (MDF). IForest (Viterbo). 2014; 8(5):677-680.

31.

Taskirawati I., Agussalim A., Baharuddin B., Suhasman S. Characteristics of the Cement Board Using CO2 Injection Technology from Wood and Non-Wood Species. IOP Conference Series: Materials Science and Engineering. 2019IOP Publishing.

32.

Tsoumis G. Science and technology of wood. Structure, properties, utilization. 1991 New York, USA: Van Nostrand Reinhold. .

33.

Wu Q., Suchsland O. Linear expansion and its relationship to moisture content change for commercial oriented strandboards. Forest Products Journal. 1996; 46(11/12):79-83.

34.

Xu W., Suchsland O. Linear expansion of wood composites: A model. Wood and Fiber Science. 1997; 29(3):272-281.

35.

Yanti H., Massijaya M.Y., Cahyono T.D., Novriyanti E., Iswanto A.H. Fundamental Properties of Composite Board Made with Oriented Strand Board and Three Different Species of Veneer. Journal of the Korean Wood Science and Technology. 2019; 47(2):239-248.

36.

Zhang Y-h., Huang Y-x., Ma H-x., Yu W-j., Qi Y. Effect of Different Pressing Processes and Density on Dimensional Stability and Mechanical Properties of Bamboo Fiber-based Composites. Journal of the Korean Wood Science and Technology. 2018; 46(4):355-361.