| Tensile σ ultimate (MPa) | Number of sample without node | 5 | 3 | 320 | 6 | 147 |
| CoV internode | 30.58% | 10.38% | 24.50% | 5.42% | 6.30% |
| Number of sample with node | 5 | 3 | - | 6 | 167 |
| CoV node | 26.08% | 9.05% | - | 9.36% | 8.80% |
| Tensile modulus of elasticity ET (MPa) | Number of sample without node | 5 | 3 | 320 | - | - |
| CoV internode | 13.21% | 4.12% | 15.40% | - | - |
| Number of sample with node | 5 | 3 | - | - | - |
| CoV node | 25.41% | 14.08% | - | - | - |
| Compressive σ ultimate (MPa) | Number of sample without node | 3 | 4 | - | 12 | 231 |
| CoV internode | 6.76% | 9.47% | - | 7.05% | 8.20% |
| Number of sample with node | 2 | 4 | - | 12 | 74 |
| CoV node | 0.81% | 25.76% | - | 9.16% | 6.90% |
| Compressive modulus of elasticity EC (MPa) | Number of sample without node | 3 | 4 | - | - | 231 |
| CoV internode | 20.25% | 40.03% | - | - | 8.70% |
| Number of sample with node | 2 | 4 | - | - | 74 |
| CoV node | 11.25% | 52.67% | - | - | 8.00% |