Table 3. Statistical analysis of the mechanical properties of clonal teak

Parameters	Value max	Value min	Mean	Sig.
Parameters	Value max	Value min	Mean	P_Axial	P_Radial	P_{Axial × Radial}
Static bending strength
MOE (GPa)	11.50	6.94	9.35	0.01^*	0.00^*	0.43^ns
MOR (MPa)	92.91	46.09	72.00	0.29^ns	0.03^*	0.99^ns
CS parallel to grain (MPa)	45.05	30.33	37.93	0.01^*	0.00^*	0.02^*
CS perpendicular to grain (MPa)	24.23	10.29	13.45	0.06^*	0.00^*	0.020^*
Hardness (MPa)	25.98	12.01	19.29	0.063^ns	0.036^*	0.193^*
Cleavage strength (kg/m)	763.94	360.89	554.50	0.06^ns	0.00^*	0.05^ns

No significant difference.
Siginificantly different at α = 0.5.
MOE: modulus of elasticity, MOR: modulus of rupture, CS: compressive strength.